Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Orgalloy® LT 4060 ES BLACK T6L - PA6... - ARKEMA

Check here, which other Orgalloy LT datasheets, application examples or technical articles are available in Material Data Center

加工/物理特性 - 机械性能 - 热性能 - 电性能 - 其它性能 - 函数

Any use of this information falls under the rules of our disclaimer.

材料文字说明

Orgalloy® LT 4060 ES BLACK T6L resin is a polyamide alloy especially designed for extrusion blow molding. This black grade offers an excellent thermal resistance, cold impact performance and flexibility.

Main applications:

• Automotive air intake ducts (clean air duct and outside intercooler tube)

Packaging:
This grade is delivered dried in sealed packaging (25kg bags) ready to be processed.

Shelf life:
Two years from the date of delivery. For any use above this limit, please refer to our technical services.

加工/物理特性	干 / 已调节	单位	Test Standard
ISO数据
熔体体积流动速度, MVR	0.5 / *	cm³/10min	ISO 1133
温度	235 / *	°C	-
载荷	5 / *	kg	-

机械性能	干 / 已调节	单位	Test Standard
ISO数据
拉伸模量	570 / 230	MPa	ISO 527
50％伸长率时的应力S	22 / 16	MPa	ISO 527
断裂伸长率	>50 / >50	%	ISO 527
简支梁缺口冲击强度, +23°C	79 / 78	kJ/m²	ISO 179/1eA
肖氏硬度D	50 / *	-	ISO 7619-1

热性能	干 / 已调节	单位	Test Standard
ISO数据
熔融温度, 10°C/min	220 / *	°C	ISO 11357-1/-3
热变形温度, 0.45 MPa	60 / *	°C	ISO 75-1/-2
维卡软化温度, B	62 / *	°C	ISO 306
1.5mm名义厚度时的燃烧性	HB / *	class	IEC 60695-11-10
测试用试样的厚度	1.6 / *	mm	-
厚度为h时的燃烧性	HB / *	class	IEC 60695-11-10
测试用试样的厚度	3.2 / *	mm	-

电性能	干 / 已调节	单位	Test Standard
ISO数据
相对漏电起痕指数	* / 600	-	IEC 60112

其它性能	干 / 已调节	单位	Test Standard
吸水性	5 / *	%	类似ISO 62
吸湿性	1.1 / *	%	类似ISO 62
密度	1040 / 1040	kg/m³	ISO 1183

函数

典型数据

加工方法

吹塑

供货形式

粒料, 黑色

特殊性能

经光稳处理的/耐光的, 经耐紫外线处理的/耐气候的, 经热稳处理的/耐热的

地区供应

北美, 欧洲, 亚太, 中南美洲, 中东/非洲

其他信息

吹塑成型

Processing conditions:
- Drying time (only necessary for bags opened for more than two hours): 4-8 hours at 80°C
- Extrusion melt temperature (min-recommended-max): 250-260-270°C 

耐化学性

酸类
	硫酸 (5g/100g) (23°C)
碱类
	氢氧化钠溶液 (1g/100g) (23°C)
碳氢化合物
	甲苯 (23°C)
酮类
	丙酮 (23°C)
盐溶液
	氯化锌溶液 (50g/100g) (23°C)
其它
	乙二醇水溶液 (50g/100g) (108°C)

权利义务的法律声明

Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.

Created: Source: www.materialdatacenter.com

Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.